C%: min. 0,2 – max. 0,22
Si%: max. 0,55
Mn%: max. 1,6
P%: max. 0,03
S%: max. 0,03
Cu%: max. 0,55
Mechanical proporties: for treatment +SH +N
| Diameter: | tensile test (DIN EN ISO 6892-1): | hardness | Charpy impact | ||||
|---|---|---|---|---|---|---|---|
| yield strength | tensile strength | strain | contraction | (DIN EN ISO 6506-2) | (ISO 148-1) | ||
| Re in [N/mm²] | Rm in [N/mm²] | A5 in [%] | Z in [%] | in Brinell [HB] | |||
| <16 mm | min. | 355 | 510 | ||||
| max. | 680 | ||||||
| 16 mm – 40 mm | min. | 345 | 470 | 146 HB | |||
| max. | 630 | 187 HB | |||||
| 40 mm – 63 mm | min. | 335 | 470 | 146 HB | |||
| max. | 630 | 187 HB | |||||
| 63 mm – 80 mm | min. | 325 | 470 | 146 HB | |||
| max. | 630 | 187 HB | |||||
| 80 mm – 100 mm | min. | 315 | 470 | 146 HB | |||
| max. | 630 | 187 HB |