C45+SH

Delivery condition peeled, straightened and polished according to DIN EN 10278

Goodness class

C45+SH

Material no.

1.0503

Assignment of standards

DIN EN ISO 683-1 & 10277

Treatment status

'+U +N +QT

Your contact

Marlo Welsch
Head of Sales
m.welsch@wsb-gmbh.eu
+49 (0) 23 30 / 91 656 – 30

Thomas Eger
Sales (south)
t.eger@wsb-gmbh.eu
+49 (0) 23 30 / 91 656 – 31

Analysis

C%: min. 0,42 – max. 0,5
Si%: min. 0,1 – max. 0,4
Mn%: min. 0,5 – max. 0,8
P%: max. 0,045
S%: max. 0,045
Cu%: max. 0,3
Cr%: max. 0,4
Mo%: max. 0,1
Ni%: max. 0,4
Cr+Mo+Ni: max. 0,63

Mechanical proporties: for treatment +SH

Diameter:		tensile test (DIN EN ISO 6892-1):				hardness	Charpy impact
		yield strength	tensile strength	strain	contraction	(DIN EN ISO 6506-2)	(ISO 148-1)
		Re in [N/mm²]	Rm in [N/mm²]	A5 in [%]	Z in [%]	in Brinell [HB]
16 mm – 100 mm	min.		580			172 HB
	max.		820			241 HB

Mechanical proporties: for treatment +N

Diameter:		tensile test (DIN EN ISO 6892-1):				hardness	Charpy impact
		yield strength	tensile strength	strain	contraction	(DIN EN ISO 6506-2)	(ISO 148-1)
		Re in [N/mm²]	Rm in [N/mm²]	A5 in [%]	Z in [%]	in Brinell [HB]
<16 mm	min.	340	620	14%
	max.
16 mm – 100 mm	min.	305	580	16%
	max.
100 mm – 250 mm	min.	275	560	16%
	max.

Mechanical proporties: for treatment +QT

Diameter:		tensile test (DIN EN ISO 6892-1):				hardness	Charpy impact
		yield strength	tensile strength	strain	contraction	(DIN EN ISO 6506-2)	(ISO 148-1)
		Re in [N/mm²]	Rm in [N/mm²]	A5 in [%]	Z in [%]	in Brinell [HB]
16 mm – 40 mm	min.	430	650	16%	40%
	max.		800
40 mm – 100 mm	min.	370	630	17%	45%
	max.		780

Information is without guarantee of correctness and completeness.