C%: min. 0,32 – max. 0,39
Si%: min. 0,1 – max. 0,4
Mn%: min. 0,5 – max. 0,8
P%: max. 0,025
S% C35E: max. 0,035
S% C35R: min. 0,02 – max. 0,04
Mo%: max. 0,1
Cr%: max. 0,4
Ni%: max. 0,4
Cu%: max. 0,3
Mechanical proporties: for treatment +N
| Diameter: | tensile test (DIN EN ISO 6892-1): | hardness | Charpy impact | ||||
|---|---|---|---|---|---|---|---|
| yield strength | tensile strength | strain | contraction | (DIN EN ISO 6506-2) | (ISO 148-1) | ||
| Re in [N/mm²] | Rm in [N/mm²] | A5 in [%] | Z in [%] | in Brinell [HB] | |||
| <16 mm | min. | 300 | 550 | 18% | |||
| max. | |||||||
| 16 mm – 100 mm | min. | 270 | 520 | 19% | |||
| max. | |||||||
| 100 mm – 250 mm | min. | 245 | 500 | 19% | |||
| max. |
Mechanical proporties: for treatment +QT
| Diameter: | tensile test (DIN EN ISO 6892-1): | hardness | Charpy impact | ||||
|---|---|---|---|---|---|---|---|
| yield strength | tensile strength | strain | contraction | (DIN EN ISO 6506-2) | (ISO 148-1) | ||
| Re in [N/mm²] | Rm in [N/mm²] | A5 in [%] | Z in [%] | in Brinell [HB] | |||
| 16 mm – 40 mm | min. | 370 | 600 | 19% | 35 | ||
| max. | 750 | ||||||
| 16 mm – 63 mm | min. | 320 | 550 | 20% | 35 | ||
| max. | 700 | ||||||
| 63 mm – 100 mm | min. | 320 | 550 | 20% | 35 | ||
| max. | 700 |