C%: min. 0,12 – max. 0,18
Si%: min. 0,15 – max. 0,4
Mn%: min. 0,3 – max. 0,6
P%: max. 0,025
S%: min. 0,020 – max. 0,040
Cu%: max. 0,3
Cr%: max. 0,4
Mo%: max. 0,1
Ni%: max. 0,4
Mechanical proporties: for treatment +SH
Diameter: | tensile test (DIN EN ISO 6892-1): | hardness | Charpy impact | ||||
---|---|---|---|---|---|---|---|
yield strength | tensile strength | strain | contraction | (DIN EN ISO 6506-2) | (ISO 148-1) | ||
Re in [N/mm²] | Rm in [N/mm²] | A5 in [%] | Z in [%] | in Brinell [HB] | |||
16 mm – 100 mm | min. | 330 | 98 HB | ||||
max. | 600 | 178 HB |