C%: min. 0,42 – max. 0,5
Si%: max. 0,4
Mn%: min. 0,7 – max. 1,1
P%: max. 0,06
S%: min. 0,15 – max. 0,25
Mechanical proporties: for treatment +SH
Diameter: | tensile test (DIN EN ISO 6892-1): | hardness | Charpy impact | ||||
---|---|---|---|---|---|---|---|
yield strength | tensile strength | strain | contraction | (DIN EN ISO 6506-2) | (ISO 148-1) | ||
Re in [N/mm²] | Rm in [N/mm²] | A5 in [%] | Z in [%] | in Brinell [HB] | |||
16 mm – 40 mm | min. | 590 | |||||
max. | 760 | 222 HB | |||||
40 mm – 63 mm | min. | 580 | |||||
max. | 730 | 213 HB | |||||
63 mm – 100 mm | min. | 560 | |||||
max. | 710 | 207 HB |